| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 比重 | --- | ASTM D-792 | 1.2 | --- | |
| 物理性能 | 吸水率 | 23°C水中24小时 | ASTM D-570 | 0.2 | % | |
| 透光率 | 厚度3mm | ASTM D-1003 | 89 | % | ||
| 折射率 | --- | ASTM D-542 | 1.585 | --- | ||
| 成型收缩率 | 流动方向 | ASTM D-955 | 0.5~0.7 | % | ||
| 成型收缩率 | 垂直方向 | ASTM D-955 | 0.5~0.7 | % | ||
| 机械性能 | 负荷-挠曲温度 | 负荷0.451MPa(4.6kgf/cm) | ASTM D-648 | 146 | ℃ | |
| 洛氏硬度 | M标度 | ASTM D-785 | 77 | --- | ||
| 弯曲模量 | --- | ASTM D-790 | 2190(22300) | Mpa(kgf/cm2) | ||
| 压缩强度 | --- | ASTM D-695 | 75(760) | Mpa(kgf/cm2) | ||
| 耐冲击强度值 | 艾氏、带缺口厚度3.2mm | ASTM D-256 | 930(95) | j/m(kgf?cm/cm) | ||
| 耐冲击强度值 | 艾氏、带缺口厚度6.4mm | ASTM D-256 | 160(16) | j/m(kgf?cm/cm) | ||
| 拉伸强度 | 屈服 | --- | ASTM D-638 | 60(610) | Mpa(kgf/cm2) | |
| 断裂 | ASTM D-638 | 84(860) | Mpa(kgf/cm2) | |||
| 拉伸模量 | --- | ASTM D-638 | 2090(21300) | Mpa(kgf/cm2) | ||
| 拉伸率 | 屈服 | --- | ASTM D-638 | 6 | --- | |
| 断裂 | ASTM D-638 | 130 | ||||
| 弯曲强度 | --- | ASTM D-790 | 87(890) | Mpa(kgf/cm2) | ||
| 负荷-挠曲温度 | 负荷-挠曲温度 | ASTM D-648 | 136 | ℃ | ||
| 电气性能 | 绝缘破坏强度 | 快速加压值厚度1.6mm | ASTM D-149 | 30 | KV/mm | |
| 体积电阻率 | --- | ASTM D-257 | 3 | ×1016Ω.cm | ||
| 介电率 | 60Hz | ASTM D-150 | 2.95 | --- | ||
| 介电率 | --- | ASTM D-150 | 0.009 | 106Hz | ||
| 耐电弧性 | --- | ASTM D-495 | 110 | sec | ||
| 耐导电径迹性（CTI | --- | IEC 112 | 300 | V | ||
| 阻燃性 | 厚度1.47mm | UL 94 | 94V-2 | --- | ||
| 阻燃性 | 厚度3.05mm | UL 94 | 94V-2 | --- | ||
| 热 性 能 | 温度指数 | 电学式 | 厚度1.47mm | UL 746B | 125 | ℃ |
| 冲击式 | 厚度1.47mm | UL 746B | 115 | ℃ | ||
| 非冲击式 | 厚度1.47mm | UL 746B | 125 | ℃ | ||
| 线膨胀系数 | 垂直方向 | ASTM D-696 | 7 | ×10-5cm/cm/℃ | ||
| 线膨胀系数 | 流动方向 | ASTM D-696 | 7 | ×10-5cm/cm/℃ | ||
以上嘉兴\日本帝人PC K-1300塑料物性参数仅供参考，轻易实际操作为准！